Graphite electrode raw material-binder

Binder is one of the raw materials of graphite electrode

The binder function has two aspects:
1. When it is in liquid state, the carbonaceous aggregate and powder are wetted, bonded and kneaded into a plastic paste. After the paste is formed under pressure and cooled, the binder is hardened and the aggregate and powder are consolidated into a green .
2. The green body is fired at a high temperature, at this time the binder participates in the carbonization reaction and forms a good solid state combination, so that the product obtains a fixed geometry. The binder is within the appropriate temperature range
It is a flowable liquid that can be absorbed by carbonaceous aggregates and powders and can penetrate into the voids of aggregates and powders, and knead to form a plastic paste within a certain temperature range. This paste has a good Viscoelasticity and lubricity.
Viscoelasticity means that the material flows viscously under a certain temperature or under long-term load, while it has elasticity under low-temperature or short-time load. Viscoelasticity has a certain influence on the molding effect (compression effect). Lubricity refers to the
The mutual position of the aggregate particles is easy to move. After being filled with each other to form a stable arrangement, the aggregate particles can be prevented from being crushed. The paste should have good plastic deformation ability during the molding process
After cooling, the green body is in a hardened state after cooling. During this change, the green body should not have some sharp changes in its shape (such as expansion and contraction). When the green body is roasted, the binder is heated to a certain temperature and becomes liquid again.
After a long time of pyrolysis and polycondensation, it is finally carbonized into pitch coke, and at the same time, the aggregate and powder are firmly combined. The coke left in this carbonization process should be as much as possible (ie, the coking value is high). During roasting
The green body should not produce larger volumetric shrinkage expansion (excessive shrinkage expansion will cause cracking of the roasted product).
For the production of Graphite Electrodes, it is desirable that the coke after the carbonization of the binder is easy to graphitize, and has a linear expansion coefficient similar to that of carbonaceous aggregates at high temperatures for graphitization.


  • The second largest in the country
  • Cumulative supply unit 330+
  • Cost-effective than the peer 20%
  • 48H rushed to the production site as soon as possible
  1. UHP600X2400MM Graphite Electrode 200 tons in StockComing the end of this year, we have achieved a wonderful sale target even under corona impact. Right now we h.

  2. The electrode paste is burned in a submerged electric furnace (sintered in an electrode barrel made of steel plate) and consumed, so it is also called a continu.

  3. This week, 250 tons cylinder electrode paste 500x1000mm was finished and delivered to our Middle East customer. This customer is a high carbon ferrochrome prod.

Leave Your Comment